Spring Steel Wire Process

(Steel) surface treatment----drawing of wire rod (mattress wires available this method)

Patented spring wires: in the middle of wire sizes, or cold-drawn spec lead hardening and surface treatment and drawing.

Galvanized spring steel wire: usually hot-dip galvanizing or plating finished size, also use wire pickling hot-cold-drawn after galvanizing to the required size.

Oil hardened spring steel wire: on-demand can be made of carbon steel or alloy steel, surface treatments and quenched and tempered after cold drawing to a finished size, this kind of technology in automotive suspension coil spring and valve spring steel wire with more ordinary Springs, of course, can also be used.

Surface treatment: commonly used pickling and phosphorization, removal of ironoxide to form phosphate coating; there are a few mechanical approach. Aim was to meet the requirements of cold-drawn wire-drawing process, smooth surface is obtained. Spring steel wire for high fatigue life, such as valve spring steel wire, steel wire rod herein, reducing surface defects on steel billet grinding, also help reducedefects.

Drawing: finished pulling thread drawing process has a great influence on the product properties, generally use larger total area reduction of about 90% (see area reduction rate) and low pass area reduction (10%-20%), in order to ensure the toughness of the product. For high strength spring steel wire, drawing for the controlof exports of steel temperature below 150 ° c, preventing wire reverse due to strain aging crack, which is a major flaw of steel scrap. For this reason, drawing a good lubrication is required and sufficient cooling, small lane area reduction and drawing speed helps reduce the wire's temperature rise.

Heat treatment: carbon steel Spring wire lead hardening process, you can get veryfine Pearlite (sorbite) for the improvement of deep drawing and spring propertiesare useful, patenting of the alternative process of fluidized-bed is not extended, only in small diameter application. Alloy steel wire annealing heat treatment is generally used to make drawing deformation microstructure adapted. Stainless steel wire heat treatment solution treatment, the purpose of which is to improve the Organization to meet the needs of drawing. Oil quenching process used on the wire using induction heating or gas, fuel oil furnace, heating the wire to the austenitizing temperature insulation for some time, another medium-temperature tempering afterhardening. Although nominally called oil, basically by water quenching or add polymer water quenching.