Oil Hardened Brush Steel Wire 0.3mm 0.35mm 0.4mm

Using my products to create value for you is our company's philosophy as always. Our goal is to provide our customers with higher quality and cost-effective 65Mn tempering spring steel wire ASTM-A230-99, ASTTM229A-229M-99 spring steel wire, 60si2mna alloy spring steel wire EN10270-2. We keep pace with the times, explore market demand in depth, and continuously invest in research and development of new styles and products that strive for excellence. We've our private experienced R&D enginners to meet any of one's requriements. Our company philosophy is the pursuit of excellence and sustainable operation. Under the guidance of the spirit of speed, punctuality and service, we continue to provide more considerate services, and always put the interests of customers first. We give full play to R&D advantages in design, focusing on every minute detail, safety hazard control, etc.

Quick Details

Steel Grade: 65mn 60si2mna 55crsi(SAE9254V) 50crva

Standard: AISI, ASTM, BS, DIN, JIS

Product name: super supplier of high carbon spring steel wire

Surface: bright

Tensile strength: 1340mpa-2230mpa

Usage: Valve springs, valve springs, clutch springs, coil springs, spring rails, car springs, etc.

Certificate: ISO 9001:2008

Package: in coil

Diameter: 0.5mm-10mm

Spring steel wire Uses:

Spring wire is mainly used in locomotives, vehicles, automobiles, tractors, aircraft and a variety of coil spring spring.

Hot forming spring heat treatment diameter or plate thickness greater than 10-15mm large spring, multi-purpose hot-rolled wire drawn wire rod or steel plate made of.

Processing and heat treatment: the first spring steel wire heated to a temperature higher than the normal quenching temperature of 50-80 ℃ under the conditions of hot-rolled forming, and then quenched in the tempering tempering, to obtain excellent flexibility and fatigue strength of the tempering sorbite. Spring steel wire quenching heating should be used with less oxygen or no oxidation equipment such as salt bath furnace, protective atmosphere furnace, to prevent oxidation decarburization.

Spring steel wire after heat treatment should also be shot peening, strengthen the surface, resulting in residual compressive stress, improve fatigue strength.

Hot-rolled spring steel wire used in the process are: flat steel cut -> heat bending forming after heat quenching + tempering + shot peening -> packaging.

Cold forming spring heat treatment diameter of less than 8mm of the spring, cold-rolled steel wire commonly used cold-rolled forming. Cold-drawn steel wire manufacturing process and follow-up heat treatment, mainly in the following three categories:

① lead bath cold drawn steel wire drawing the first three consecutive wire drawing, the total deformation of 50%, followed by heating to Ac3 above the temperature of its austenitizing, followed by 450-550 ℃ lead bath in the isothermal treatment, Body into sorbite tissue. Yield strength of 1600Mpa, cold roll forming, annealing at 200-300 ℃ stress can be.

② oil quenching and tempering steel wire drawing to size, the oil quenching and tempering. The strength of such wire is inferior to that of lead-treated steel wire, but the performance is uniform and the cost is low. After cold roll forming, a stress-relieving treatment is performed.

③ annealed steel wire drawing the wire to the required size, and then annealing. After the softening of the cold-rolled steel wire forming, subject to quenching after tempering in the temperature to get the required mechanical properties. Alloy elements in the spring wire in the main role is to improve the mechanical properties, improve process performance and to give some special properties (such as high temperature, corrosion resistance) and so on.

Generally customer-oriented, and it's our ultimate goal for Oil Hardened Brush Steel Wire 0.3mm 0.35mm 0.4mm. With the long-term efforts and active investment of company members, our company's strength has been recognized by the industry. Our business philosophy is 'manufacturing high-quality goods, serving the world', all employees warmly welcome to cooperate with friends at home and abroad to create brilliant.