We produce Mechanical steel wire JIS G3561, 50crva steel wire JIS G3561, 60si2mna steel wire factory throughout the world, and we will continue for the new old customer service in line with the practical, high quality, innovation and progress of spirit. We absorb and utilize powerful human resources as a backing, and also pay attention to the investment of talents and technological transformation. Flexible, fast and quality customer service is the focus of our business strategy. Our products are sold to the Middle East, Southeast Asia, Africa, Europe, America and other regions, and are favorably appraised by clients. We always firmly believe that only by taking the lead in innovation can we always maintain the leading position of the brand. At the same time, we regard 'product quality' as the basis for the survival and development of enterprises.

Oil - hardened steel wire - Practical procedure

Production process

Line - anaerobic heating - oil quenching - tempering - water cooling - coated anti-rust oil - The line

(A) pay-off

According to the requirements of a single verification process oil quenched steel semi-finished steel, specifications,

Surface Quality,

Unqualified material is not put into production;

Steel wire

Lifting should be to ensure smooth, put the line smooth, wear the wire when used as a lead wire.

In order to minimize the furnace pipe and the furnace mouth scaling, to try not to use rusty wire, not into the thin wire; also

To minimize the dirt on the wire, so the wire into the stove before going through the decontamination device.

(B) of the furnace temperature set by the process requirements, should ensure that there are protective gas furnace tube,

, That is, the furnace tube outlet should be a fire. Protective gas for

Liquid ammonia in the catalyst under the action of heating

75%

Of hydrogen and

25%

Of nitrogen. which is:

2NH

3

--- →

3H

2

+ & Gt;

2   

temperature reflex:

800

Lt; 0 & gt; C

~ 830

Lt; 0 & gt; C

In order to minimize the stove fouling, consider the use of slotted steel tube in the mouth, and often turn, descaling.

(C) oil quenching

Steel oil quenching, should ensure that the oil surface above the steel ≥

4cm

, But can not be quenching oil overflow tank, but can not enter the furnace

Body, to ensure production safety,

Steel wire out of the tank,

Should be attached to the oil on the wire should be wiped clean. Often observed quenching oil

Box oil level, not enough time to add.

In order to minimize the quenching oil on the wire into the tempering furnace, increase the oil removal device.

(D) tempering

Furnace temperature set according to process requirements, the wire can not be staggered in the furnace, to comb smooth, lead pot entrance, as the wire with

Residual oil, a long time will be on fire, dry powder extinguishing agent extinguished, agglomeration of the covering agent should be removed, add new.

(5) water cooling

Steel wire tempering should ensure that water cooling, and residual water drying, so as to avoid steel rust.

(6) anti-rust oil

In order to prevent the rust of steel wire, steel wire should be evenly coated with a layer of anti-rust oil in the book.

(7) close line

Take-up speed set according to process requirements, wear the first use of waste silk should be all cut off, due to failure shutdown should also be cut off furnace midline,

All electrical connections in the production process must be cut off.

When the wire is pulled off, to cut off the wire diameter failed parts.

Wire should be guaranteed that the dead wire does not bend,

No mechanical scratches, disc shape should be structured; in the completion of this class production of steel wire packaging,

want

Cut out

30

Cm long tail wire for testing, and the tail wire to stay out

5 to 10

Cm for reference purposes

, Hang tags,

Do the original record.

(Eight)

Detection

So that each wire are detected, testing items for the wire diameter check, tensile strength, shrinkage, and other necessary items.

Do the original record. 

After testing to check the wire diameter on the label, write on the tensile strength, date.

With wide experience and expertise, Friend Metal is engaged in the developing, manufacturing and marketing of mechanical valves - silicon - manganese - chromium - vanadium - chromium - silicon alloy spring wire ASTM-A230-99, ASTM-A401, EN10270-2, JIS G3561. As a professional manufacturer, we now brings you high quality various steel wires made in China which comes in high strength, well toughness and excellent wearing resistance. We also welcome your customized orders.

Facing new challenges in the future market, all our employees will continue to carry forward a professional, efficient, enthusiastic and thoughtful work style, and provide customers with reliable and high-quality Valve Compression Springs Engine Valve Springs Sport Lowering Springs Barrel Style Springs with Tapered Ends Metal Springs Wire Form Springs and timely services. In the days to come, we will definitely go forward, work diligently, keep pace with the times, cooperate with new and old customers, and move forward side by side. We will constantly update our company concept to create quality products to meet market demands.