The lubrication condition has an important influence on the service life of the wire rope, and the lubrication of the steel wire rope is maintained, so that it is always in good lubrication condition, and its service life can be extended by two to three times.
Introduces lubrication on the service life of wire rope and carries on the analysis of impact mechanism, lead to poor lubrication between the internal steel wire rope friction factor increases, the fretting wear of steel wire speed is accelerated, lubrication failure resulted in the corrosion rate of steel wire speed up at the same time, wear and corrosion are there wire cross-sectional area is reduced, wire rope by the axial force to produce stress concentration on the wear and tear, that cause the abrasion damage initiation of fatigue cracks, significantly reduce the service life of wire rope.
The fatigue and corrosion fatigue are the main reasons for the failure of wire rope.
It is a new way to prolong the service life of wire rope.